Recent developments in high Curie temperature perovskite single crystals

The temperature behavior of various relaxor-PT piezoelectric single crystals was investigated. Owing to a strongly-curved morphotropic phase boundary, the usage temperature of these perovskite single crystals is limited by T/sub R-T/- the rhombohedral to tetragonal phase transformation temperature - which occurs at the significantly lower temperatures than the Curie temperature T/sub c/. Attempts to modify the temperature usage range of Pb(Zn/sub 1/3/Nb/sub 2/3/)O/sub 3/-PbTiO/sub 3/ (PZNT) and Pb(Mg/sub 1/3/Nb/sub 2/3/)O/sub 3/-PbTiO/sub 3/ (PMNT) rhombohedral crystals (T/sub c/ /spl sim/ 150-170/spl deg/C, T/sub R-T/ /spl sim/ 60-120/spl deg/C) using minor dopant modifications were limited, with little success. Of significant potential are crystals near the morphotropic phase boundary in the Pb(Yb/sub 1/2/Nb/sub 1/2/)O/sub 3/-PbTiO/sub 3/ (PYNT) system, with a T/sub c/ > 330/spl deg/C, even though T/sub R-T/ was found to be only half the value at /spl sim/160/spl deg/C. Single crystals in the novel BiScO/sub 3/-PbTiO/sub 3/ system offer significantly higher T/sub c/s > 400/spl deg/C, while exhibiting electromechanical coupling coefficients k/sub 33/ > 90% being nearly constant till the T/sub R-T/ temperature around 350/spl deg/C, which greatly increases the temperature range for transducer applications.