Conducting metallic oxide contacts on superconducting YBa/sub 2/Cu/sub 3/O/sub 7-x/ thin films

Low resistance contacts to superconducting YBa/sub 2/Cu/sub 3/O/sub 7-x/ (YBCO) thin films have been prepared by using conducting metallic ruthenium oxide, RuO/sub 2/, as contact electrodes. The surface specific contact resistivity of the best contacts made by DC magnetron sputtering of RuO/sub 2/ and a structure of Au/RuO/sub 2/ or Ag/RuO/sub 2/ on YBCO thin films has an upper limit value in the range of 5*10/sup -8/ Omega -cm/sup 2/ but less than 5*10/sup -6/ Omega -cm/sup 2/ at 77 K for a single layer RuO/sub 2/ on YBCO thin films. Auger depth profiling shows diffusion of Y, Ba, and Cu into RuO/sub 2/ but no apparent diffusion of Ru into YBCO thin films after thermal treatment of the contact at 500 degrees C. No degradation of zero resistance temperature was seen for the superconducting thin films after the formation of the low resistance contacts. No special pretreatment of the YBCO film surface was required prior to depositing the contact electrodes, but a post-deposition anneal was necessary to obtain a good contact.<
>