Remanence loss in γ-Fe2O3tapes as related to reptation, viscosity, and print-through

The reptation and magnetic viscosity in γ-Fe
2
O
3
tape as a function of an applied field is found by using a rotating sample magnetometer (RSM) which measures the decrease in remanent magnetization M
R
, as the sample spins in a field at different frequencies. A modified RSM is used to find the decrease in M
R
when a reverse field is repeatedly applied along a stationary axis. Reptation is found only when the sample rotates in a field. Magnetic viscosity effects peak at fields near the coercive field and scale with print-through in tapes.