GaInNAs/GaAs quantum well lasers grown by solid-source molecular beam epitaxy

The growth of GaInNAs/GaAs quantum wells (QW) was investigated by solid-source molecular beam epitaxy. N was introduced by a dc-active plasma source. The effect of growth conditions such as on the N incorporation and photoluminescence (PL) intensity of the QWs has been studied. The PL peak intensity decreased and the PL full width at half maximum increased with increasing N concentrations. The highest N concentration of 2.6% in a GaInNAs/GaAs QW was obtained, and corresponding to a PL peak wavelength of 1.57 /spl mu/m at 10K. Rapid thermal annealing at 850/spl deg/C significantly improved the crystal quality of the QWs. An optimum annealing time of 5s at 850/spl deg/C was obtained. A GaInNAs/GaAs SQW laser with the emitting wavelength of 1.2 /spl mu/m and a high characteristic temperature of 115 K was achieved at room temperature.